ISO 6361-2-2014 pdf free download

ISO 6361-2-2014 pdf free download.Wrought aluminium and aluminium alloys — Sheets, strips and plates — Part 2:Mechanical properties
Aluminium et alliages daluminium corroyés — Tôles, bandes et tôles épaisses — Partie 2: Propriétés mécaniques.
In conjunction with ISO 6361-1. this part of Iso 6361 specifies the mechanical properties of wrought
aluminium and aluminium alloy sheets, strips, and plates for general engineering applications.
It applies to flat-rolled products.
The chemical composition of these materials is given in ISO 6361-5.
The designations of aluminium and aluminium alloys and the temper designations used in this part of ISO 6361 are in accordance with ISO 2107.
NOTE In certain countries, for purposes of mechanical properties, the thickness limit can be lowered to 0,15 mm by agreement between the purchaser and the supplier, in the case of sheets and strips.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 6361-1, Wrought aluminium and aluminium alloys — Sheets, strips and plates — Part 1: Technical conditions for inspection and delivery
3 Terms and definitions
For the purposes of this docLiment, the terms and definitions given in ISO 6361-1 apply.
4 Tensile testing
For the selection of the specimens and tensile testing, see ISO 6361-1.
5 Bend testing
For the selection of the specimens and bend testing, see ISO 6361-1.
6 Mechanical properties
6.1 Tensile test
Values for mechanical properties of aluminium and aLuminium alloys are given in TithIesl to 6. For elongation, two different gauge lengths are used. The choice of the gauge length for elongation measurements (A orAsomni) is at the discretion of the producer, unless otherwise agreed.
NOTE A is the percentage elongation on a gauge length of 5,65 . /lSOmm is the percentage elongation on
a gauge length of 50 mm.
Test results shall be rounded in accordance with the rules given in Annex A.
6.2 Bend test
Sheet, strip, and plate shall be capable of being bent cold through an angle of 180°, as applicable, around a pin having a radius equal to k times the thickness, t, of the sheet, strip, or plate (for example O,5t) without cracking. The values of the minimum bend radii for different alloys, tempers, and thicknesses are given in Tables 1 to
NOTE The explanations of the numbered notes in Tables ito 63 are given after Table 63.ISO 6361-2-2014 pdf free download.