ISO 8496-2013 pdf free download.Metallic materials — Tube — Ring tensile test
Matériaux métalliques — Tubes — Essai de traction sur anneaux.
This ISO 8496 specifies a method for a ring tensile test of tubes to reveal surface and internal defects by subjecting the test piece to strain until fracture occurs. This test may also be used to assess the ductility of tubes.
The ring tensile test Is applicable to tubes having an outside diameter exceeding 150 mm and a wall thickness no greater than 40 mm. The inside diameter shall be greater than 100 mm.
Subjecting a ring cut from the end ofa tube to strain in the circumferential direction until fracture occurs.
Use two circular pins, of equal diameter with parallel axes, and movable in relation to each other while still remaining parallel.
In principle, the diameter of the pins shall be the minimum permissible from strength considerations but, provided that the inside diameter of the tube allows, should be at least 3 times the wall thickness of the tube to be tested (see Figure 1).
4 Test piece
4.1 The test piece shall be a ring cut from the tube with the end faces perpendicular to the axis.
4.2 The length of the test piece (width of the ring) shall be approximately 15 mm. If the thickness exceeds 15 mm, the length of the test piece may be equal to the thickness.
4.3 The ends of the test piece shall be free from burrs. The edges may be rounded by filing or chamfered by other methods.
NOTE Non-rounded or non-chamfered edges are permissible, if the test result meets the test requirements.
5.1 In general, the test shall be carried out at ambient temperature within the limits of 10 °C to 35 °C. The test carried out under controlled conditions shall he made at a temperature of 23 °C ± 5 °C.
5.2 Place the ring cut from the tube over the pins. Subject the ring to strain by moving the pins away from each other at a specified rate until it fractures.
In cases of dispute, the rate shall not exceed 5 mm/s.
5.3 Interpretation of the ring tensile test shall be carried out in accordance with the requirements of the relevant product standard. When these requirements are not specified, the test piece shall be considered to have passed the test if the expected fracture behaviour was obtained and no other cracks arc visible without the use of magnifying aids.
6 Test report
A test report shall be provided when so specified in the relevant product standard. in this case, the test
report shall include at least the following information:
a) a reference to this International Standard, i.e. ISO 8496;
b) identification of the test piece;
c) dimensions of the test piece;
d) result of the test.ISO 8496-2013 pdf free download.
All resources on this website are from the Internet. It is only for personal study and research. No one is allowed to use it for any commercial purpose. If you need, please buy the genuine standard. If there is any infringement of your copyright, please contact the webmaster in time, and I will correct it immediately.
- Maybe you like
- Latest Updates
- ISO 287-2009 pdf free download
- ISO 527-5-2009 pdf free download
- ISO 659-2009 pdf free download
- ISO 660-2009 pdf free download
- ISO 712-2009 pdf free download
- ISO 725-2009 pdf free download
- ISO 730-2009 pdf free download
- ISO 927-2009 pdf free download
- ISO 2041-2009 pdf free download
- ISO 3040-2009 pdf free download
- ISO 3506-2-2009 pdf free download
- ISO 3506-3-2009 pdf free download